Thixotropic Resins
WorléeThix
Acrylic resins, solvent-based, thixotropic
With the thixotropic WorléeCryl grades, the rheological properties of the 2-component coatings can be excellently controlled and thus form a good addition to the formulations.
| Product | OH content on solid resin [%] | Mod. | Viscosity optical | Delivery forms [%] | Applications/properties |
|---|---|---|---|---|---|
| WorléeThix A 1420 | 2.0 | Urea | Thixotropic soft gel | 50 in BAc | WorléeThix A 1420 can be combined with air and forced drying 2K wood and plastic paints. After curing, paint films are obtained that exhibit hardness, chemical resistance and weather resistance. |
| WorléeThix A 2125 | 2.5 | Urea | Thixotropic gel | 50 in xylene | Thixotropic styrene acrylate for thick-film systems and effect paints, extremely weather-resistant. Even at room temperature drying, paint films are obtained that exhibit high hardness, chemical resistance and extreme weather resistance. |
| WorléeThix A 2126 | 2.3 | Urea | Thixotropic gel | 60 in xylene | WorléeThix A 2126 can be combined with air and forced drying metal, wood and plastic paints. Even room temperature drying produces paint films with high hardness, chemical resistance and extreme weather resistance. |
| 60 in MPA | |||||
| 60 in BAc | |||||
| WorléeThix A 2313 | 1.3 | Urea | Thixotropic soft gel | 60 in aromat. KW 155–180 | WorléeThix A 2313 can be used for air-drying and forced drying industrial coatings, or in combination with other hydroxyacrylates. Even when dried at room temperature, coating films are obtained that exhibit high hardness, chemical resistance, and very good weather resistance. |
WorléeThix
Alkyd resins, solvent-based, thixotropic
The thixotropic alkyd resins have a significant influence on the processing properties of the coating systems. Due to the different oil lengths, different fatty acids and the modification with urea or polyamide, there is a wide range to choose from. Thixotropy is formed via hydrogen bonds between the NH atoms. In the case of urea-modified resins, the addition of small quantities of polar solvents can have an additional positive influence on the thixotropy effect.
| Product | Oil [%] approx | Mod. | Mod. | Acid number DIN EN ISO 3682 [mgKOH/g] | Viscosity Optical | Delivery forms [%] | Applications/properties |
|---|---|---|---|---|---|---|---|
| WorléeThix D 46 | 40 | Conj. fatty acids | Epoxy ester | max. 4 | Thixotropic soft gel | 50 in xylene | Thixotropic epoxy ester, air and oven drying, industrial, base and top coats, zinc dust paints; thixotropy is not completely degraded by and polar substances. |
| WorléeThix L 7904 | 79 | Linseed oil | Urea | max. 15 | Thixotropic strong gel | 94 in xylene | High-solids clear coats, wood stains, high-solids primers |
| WorléeThix L 8050 | 80 | Linseed oil fatty acids | Polyamide | max. 15 | Thixotropic soft gel | approx. 100 | Thixotropic, long oil alkyd resin, for wood stains, can also be used as a sole binder. |
| WorléeThix MH 439 | 39 | Special mixed oil fatty acids | Urea | max. 25 | Thixotropic strong gel | 60 in xylene | WorléeThix MH 439 is a short oil, thixotropic alkyd resin for fast drying primers, top coats and effect paints. The gel structure cannot be completely removed by adding polar solvents or by applying heat. |
| WorléeThix S 6357 | 64 | Soybean oil | Urea | max. 15 | Thixotropic soft gel | 40 in entaromat. KW 180–220 | Thixotropic, long oil alkyd resin, combination resin for architectural coatings, wood stains (thick layer); thixotropy is not completely degraded by and polar substances. |
| 40 in Tb 180–210 | |||||||
| WorléeThix S 6358 R | 64 | Soybean oil | Urea | max. 15 | Soft gel | 50 in entaromat. KW 180–220 | WorléeThix S 6358 R is a long oil, thixotropic alkyd resin for paints and building lacquers as well as wood stains (thick layer). The gel structure is not completely degradable due to the addition of polar and heat. |
| WorléeThix S 6657 | 63 | Special vegetable fatty acids | Urea | max. 15 | Thixotropic soft gel | 60 in entaromat. KW 180–220 | Thixotropic combination resin for the production of rust-protection primers, paints,decorative coatings, and architectural varnishes, as well as for wood glazes (thick film). The gel structure is not completely degradable by the addition of polar solvents or by the application of heat. |
| WorléeThix S 6658 | 66 | Special vegetable fatty acids | Urea | max. 15 | Soft gel | 70 in entaromat. KW 180–220 | High-solids, long-oil, thixotropic alkyd resinfor the production of rust-protection primers, paints, decorative coatings, and architectural varnishes, as well as wood stains. The gel structure is not completely degradable by the addition of polar solvents or heat. The content of renewable raw materials is approximately 45 % in the supplied form. |
| WorléeThix SD 6051 | 60 | Special fatty acids | Polyamide | max. 15 | Thixotropic gel | 55 in entaromat. KW 160–200 | Like WorléeThix V 747, but with improved resistance to polar substances, particularly suitable for undercoats, thick-film rust protection systems, gloss and satin finishes. |
| WorléeThix 670hs | 61 | Special mixed fatty acids | Polyamide | max. 15 | Thixotropic gel | 70 in entaromat. KW 160–200 | WorléeThix 670 hs is a thixotropic, long-oil alkyd resin for undercoats, fillers, gloss finishes, and semi-gloss finishes, with a low VOC content. The content of renewable raw materials is approximately 41 % in the as-supplied form. |
| WorléeThix V 727 | 63 | Special mixed fatty acids | Polyamide | max. 15 | Thixotropic gel | 52 in isopar. KW 170–200 | Thixotropic long oil alkyd for undercoats, gloss paints and silk gloss paints, wall paints, as well as wood stain and rust protection paints. |
| 52 in entaromat. KW 180–220 | |||||||
| WorléeThix V 747 | 64 | Special fatty acids | Polyamide | max. 15 | Thixotropic gel | 52 in isopar. KW 170-200 | WorléeThix V 747 is a thixotropic, long oil alkyd resin, mainly for use in primers, matt wall paints, silk gloss paints and for thixotropic glossy paints and architectural coatings. WorléeThix V 747 can also be used to produce thick-film rust protection systems for heavy-duty corrosion protection. |
| 52 in entaromat. KW 180–220 | |||||||
| WorléeThix V 800 | 62 | Special mixed fatty acids | Urea | max. 15 | – | 50 in entaromat. KW. 160–200 | WorléeThix V 800 is a thixotropic, pseudo plastic, urethanized alkyd resin. Its gel structure is not completely degradable by the addition of polar solvents or by heat. |
WorléeThix
Alkyd resin emulsions, aqueous, thixotropic
| Product | pH value | Acid number DIN EN ISO 3682 [mgKOH/g] | Viscosity, optical | Delivery forms [%] | Applications/properties |
|---|---|---|---|---|---|
| WorléeThix VP E 165 W | 6.0 – 8.0 | max. 30 | Thixotropic strong gel | 40 in water | Highly thixotropic alkyd emulsion for the production of drip-inhibited paint systems; particularly suitable for wood preservative stains. |
| WorléeThix E 166 W | 6.0 – 8.0 | max. 30 | Thixotropic gel | 40 in water | Thixotropic alkyd emulsion for the production of drip-inhibited paint systems; particularly suitable for wood preservative stains. |
| WorléeThix VP E 167 W | 6.0 – 8.0 | max. 15 | Thixotropic liquid | 27 in water | Slightly thixotropic alkyd emulsion for the production of drip-inhibited paint systems; particularly suitable for wood preservative stains. |
** The products in the table are selected from the catalog. More detailed information can be found on the Worlée-Chemie website. It should be noted that our product portfolio also includes special products that are not listed in the catalog.